Embedded SONOS based memory cells

ABSTRACT

A memory device that includes a non-volatile memory (NVM) transistor which has an indium doped channel and a gate stack overlying the channel formed in a first region of a substrate and a metal-oxide-semiconductor (MOS) transistor formed in a second region of the substrate in which the gate oxide of the MOS and the oxide layer of the NVM transistor are formed concurrently.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 14/018,026, filed Sep. 4, 2013, which claims priority to U.S. Provisional Patent Application No. 61/769,693, filed Feb. 26, 2013, and to U.S. Provisional Patent Application No. 61/825,196, filed May 20, 2013, all of which are incorporated by reference herein in their entirety.

TECHNICAL FIELD

The present disclosure relates generally to semiconductor devices, and more particularly to memory cells including embedded or integrally formed SONOS based non-volatile memory (NVM) transistors and metal-oxide-semiconductor (MOS) transistors and methods for fabricating the same.

BACKGROUND

For many applications, such as system-on-chip, it is desirable to integrate logic devices and interface circuits based upon metal-oxide-semiconductor (MOS) field-effect transistors and non-volatile memory (NVM) transistors on a single chip or substrate. This integration can seriously impact both the MOS transistor and NVM transistor fabrication processes. MOS transistors are typically fabricated using a standard or baseline complimentary-metal-oxide-semiconductor (CMOS) process flows, involving the formation and patterning of conducting, semiconducting and dielectric materials. The composition of these materials, as well as the composition and concentration of processing reagents, and temperature used in such a CMOS process flow are stringently controlled for each operation to ensure the resultant MOS transistors will function properly.

Non-volatile memory devices include non-volatile memory transistors, silicon-oxide-nitride-oxide-semiconductor (SONOS) based transistors, including charge-trapping gate stacks in which a stored or trapped charge changes a threshold voltage of the non-volatile memory transistor to store information as a logic 1 or 0. Charge-trapping gate stack formation involves the formation of a nitride or oxynitride charge-trapping layer sandwiched between two dielectric or oxide layers typically fabricated using materials and processes that differ significantly from those of the baseline CMOS process flow, and which can detrimentally impact or be impacted by the fabrication of the MOS transistors. In particular, forming a gate oxide or dielectric of a MOS transistor can significantly degrade performance of a previously formed charge-trapping gate stack by altering a thickness or composition of the charge-trapping layer. In addition, this integration can seriously impact the baseline CMOS process flow, and generally requires a substantial number of mask sets and process steps, which add to the expense of fabricating the devices and can reduce yield of working devices.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be understood more fully from the detailed description that follows and from the accompanying drawings and the appended claims provided below, where:

FIG. 1 is a flowchart illustrating an embodiment of a method for fabricating a memory cell including an embedded silicon-oxide-nitride-oxide-semiconductor (SONOS) based non-volatile memory (NVM) transistor and metal-oxide-semiconductor (MOS) transistors;

FIGS. 2A-2M are block diagrams illustrating cross-sectional views of a portion of a memory cell during fabrication of the memory cell according to the method of FIG. 1;

FIG. 2N is a block diagram illustrating a cross-sectional view of a portion of a finished memory cell including an embedded SONOS based NVM transistor and MOS transistors fabricated according to the method of FIGS. 1 and 2A-2M;

FIGS. 3A and 3B are graphs illustrating improvements in threshold voltage (V_(T)) uniformity of an NVM transistor including an indium channel according to an embodiment of the present disclosure; and

FIGS. 4A-4C are graphs illustrating basic program erase characteristics and showing improvements in endurance data retention for a memory device including an embedded SONOS based NVM transistor fabricated according to an embodiment of the present disclosure.

DETAILED DESCRIPTION

Embodiments of a memory cell including an embedded non-volatile memory (NVM) transistor and a metal-oxide-semiconductor (MOS) transistor and methods of fabricating the same are described herein with reference to figures. However, particular embodiments may be practiced without one or more of these specific details, or in combination with other known methods, materials, and apparatuses. In the following description, numerous specific details are set forth, such as specific materials, dimensions and processes parameters etc. to provide a thorough understanding of the present invention. In other instances, well-known semiconductor design and fabrication techniques have not been described in particular detail to avoid unnecessarily obscuring the present invention. Reference throughout this specification to “an embodiment” means that a particular feature, structure, material, or characteristic described in connection with the embodiment is included in at least one embodiment of the invention. Thus, the appearances of the phrase “in an embodiment” in various places throughout this specification are not necessarily referring to the same embodiment of the invention. Furthermore, the particular features, structures, materials, or characteristics may be combined in any suitable manner in one or more embodiments.

The terms “over,” “under,” “between,” and “on” as used herein refer to a relative position of one layer with respect to other layers. As such, for example, one layer deposited or disposed over or under another layer may be directly in contact with the other layer or may have one or more intervening layers. Moreover, one layer deposited or disposed between layers may be directly in contact with the layers or may have one or more intervening layers. In contrast, a first layer “on” a second layer is in contact with that second layer. Additionally, the relative position of one layer with respect to other layers is provided assuming operations deposit, modify and remove films relative to a starting substrate without consideration of the absolute orientation of the substrate.

The NVM transistor may include memory transistors or devices implemented using Silicon-Oxide-Nitride-Oxide-Silicon (SONOS) or floating gate technology.

An embodiment of a method for integrating or embedding a NVM transistor into a standard or baseline CMOS process flow for fabricating one or more MOS transistors will now be described in detail with reference to FIG. 1 and FIGS. 2A through 2M. FIG. 1 is a flowchart illustrating an embodiment of a method or process flow for fabricating the memory cell. FIGS. 2A-2L are block diagrams illustrating cross-sectional views of a portion of a memory cell during fabrication of the memory cell according to the method of FIG. 1, and FIG. 2M is a block diagram illustrating a cross-sectional view of a portion of an embodiment of the finished memory cell.

Referring to FIG. 1 and FIG. 2A, the process begins with forming a number of isolation structures 202 in a wafer or substrate 204 (step 102). The isolation structures 202 isolate the memory cell being formed from memory cells formed in adjoining areas (not shown) of the substrate 204 and/or isolate the NVM transistor being formed in a first region 206 of the substrate from one or more of the MOS transistors transistor being formed in a second region 208. The isolation structures 202 include a dielectric material, such as an oxide or nitride, and may be formed by any conventional technique, including but not limited to shallow trench isolation (STI) or local oxidation of silicon (LOCOS). The substrate 204 may be a bulk wafer composed of any single crystal material suitable for semiconductor device fabrication, or may include a top epitaxial layer of a suitable material formed on a substrate. Suitable materials include, but are not limited to, silicon, germanium, silicon-germanium or a III-V compound semiconductor material.

Generally, as in the embodiment shown, a pad oxide 209 is formed over a surface 216 of the substrate 204 in both the first region 206 and the second region 208. The pad oxide 209 can be silicon dioxide (SiO₂) having a thickness of from about 10 nanometers (nm) to about 20 nm and can be grown by a thermal oxidation process or in-situ steam generation (ISSG).

Referring to FIG. 1 and FIG. 2B, dopants are then implanted into substrate 204 through the pad oxide 209 to form wells in which the NVM transistor and/or the MOS transistors will be formed, and channels for the MOS transistors (step 104). The dopants implanted may be of any type and concentration, and may be implanted at any energy, including energies necessary to form wells or deep wells for the NVM transistor and/or the MOS transistors, and to form channels for the MOS transistors. In a particular embodiment illustrated in FIG. 2B, dopants of an appropriate ion species are implanted to form a deep N-well 210 in the second region 208 over or in which a high-voltage (HV) MOS transistor 214, such as a MOS input/output (I/O) transistor, will be formed. Although not shown, it is to be appreciated that the wells or deep wells can also be formed for the NVM transistor and/or a standard or low-voltage (LV) MOS transistor, such as a MOS transistor 212. It is further to be appreciated that the wells are formed by depositing and patterning a mask layer, such as a photoresist layer above the surface 216 of the substrate 204, and implanting an appropriate ion species at an appropriate energy to an appropriate concentration.

Channels 218 for one or more of the MOS transistors 214, 212, are formed in the second region 208 of the substrate 204. As with the well implant the channels 218 are formed by depositing and patterning a mask layer, such as a photoresist layer above the surface 216 of the substrate 204, and implanting an appropriate ion species at an appropriate energy to an appropriate concentration. For example, BF₂ can be implanted at an energy of from about 10 to about 100 kilo-electron volts (keV), and a dose of from about 1e12 cm⁻² to about 1e14 cm⁻² to form an N-type MOS (NMOS) transistor. A P-type MOS (PMOS) transistor may likewise be formed by implantation of Arsenic or Phosphorous ions at any suitable dose and energy. It is to be appreciated that implantation can be used to form channels 218, in both of the MOS transistors 214, 212, at the same time, or at separate times using standard lithographic techniques, including a patterned photoresist layer to mask one of the channels for the MOS transistors.

Next, referring to FIG. 1 and FIG. 2C a patterned tunnel mask 220 is formed on or overlying the pad oxide 209, ions (represented by arrows 222) of an appropriate, energy and concentration are implanted through a window or opening in the tunnel mask to form a channel 224 for a NVM transistor 226, and the tunnel mask and the pad oxide in at least the second region 208 removed (step 106). The tunnel mask can include a photoresist layer, or a hard mask formed, from a patterned nitride or silicon-nitride layer.

In one embodiment, the channel 224 for the NVM transistor 226 is an Indium doped channel implanted with Indium (In) at an energy of from about 50 to about 500 kilo-electron volts (keV), and a dose of from about 5e11 cm⁻² to about 5e12 cm⁻² to form a n-channel NVM transistor. As explained in greater detail below, implanting Indium to form the channel 224 of the NVM transistor 226 improves the threshold voltage (V_(T)) uniformity of the NVM transistor from a sigma of V_(T) from about 150 millivolts (mV) to about 70 to 80 mV. Alternatively, BF₂ can be implanted to form an n-channel NVM transistor, or Arsenic or Phosphorous implanted to form a p-channel NVM transistor.

A photoresist tunnel mask 220 can be ashed or stripped using oxygen plasma. A hard mask can be removed using a wet or dry etch process. The pad oxide 209 is removed, for example in a wet clean process using a 10:1 buffered oxide etch (BOE) containing a surfactant. Alternatively, the wet clean process can be performed using a 20:1 BOE wet etch, a 50:1 hydrofluoric (HF) wet etch, a pad etch, or any other similar hydrofluoric-based wet etching chemistry.

Referring to FIG. 1 and FIGS. 2D-2F, the surface 204 of the substrate 204 is cleaned or precleaned, a number of dielectric layers, such as oxide-nitride-oxide or ONO layers, formed or deposited, a mask formed on or overlying the dielectric layers, and the dielectric layers etched to form a dielectric gate stack 236 in the first region 206 (step 108). The preclean can be a wet or dry process and in this embodiment is wet process using HF or standard cleans (SC1) and SC2, and is highly selective to the material of the substrate 204. SC1 is typically performed using a 1:1:5 solution of ammonium hydroxide (NH₄OH), hydrogen peroxide (H₂O₂) and water (H₂O) at 50 to 80° C. for about 10 minutes. SC2 is a short immersion in a 1:1:10 solution of HCl, H2O2 and H₂O at about 50 to 80° C.

Referring to FIG. 2D, the dielectric or ONO deposition begins with the formation of a tunnel dielectric 228 over at least the channel 224 of the NVM transistor 226 in the first region 206 of the substrate 204. The tunnel dielectric 228 may be any material and have any thickness suitable to allow charge carriers to tunnel into an overlying charge-trapping layer under an applied gate bias while maintaining a suitable barrier to leakage when the NVM transistor is unbiased. In certain embodiments, tunnel dielectric 228 is silicon dioxide, silicon oxy-nitride, or a combination thereof and can be grown by a thermal oxidation process, using ISSG or radical oxidation.

In one embodiment a silicon dioxide tunnel dielectric 228 may be thermally grown in a thermal oxidation process. For example, a layer of silicon dioxide may be grown utilizing dry oxidation at 750 degrees centigrade (° C.)-800° C. in an oxygen containing gas or atmosphere, such as oxygen (O₂) gas. The thermal oxidation process is carried out for a duration approximately in the range of 50 to 150 minutes to effect growth of a tunnel dielectric 228 having a thickness of from about 1.0 nanometers (nm) to about 3.0 nm by oxidation and consumption of the exposed surface of substrate.

In another embodiment a silicon dioxide tunnel dielectric 228 may be grown in a radical oxidation process involving flowing hydrogen (H₂) and oxygen (O₂) gas into a processing chamber at a ratio to one another of approximately 1:1 without an ignition event, such as forming of a plasma, which would otherwise typically be used to pyrolyze the H₂ and O₂ to form steam. Instead, the H₂ and O₂ are permitted to react at a temperature approximately in the range of about 900° C. to about 1000° C. at a pressure approximately in the range of about 0.5 to about 5 Torr to form radicals, such as, an OH radical, an HO₂ radical or an O diradical, at the surface of substrate. The radical oxidation process is carried out for a duration approximately in the range of about 1 to about 10 minutes to effect growth of a tunnel dielectric 228 having a thickness of from about 1.0 nanometers (nm) to about 4.0 nm by oxidation and consumption of the exposed surface of substrate. It will be understood that in this and in subsequent figures the thickness of tunnel dielectric 228 is exaggerated relative to the pad oxide 209, which is approximately 7 times thicker, for the purposes of clarity. A tunnel dielectric 228 grown in a radical oxidation process is both denser and is composed of substantially fewer hydrogen atoms/cm³ than a tunnel dielectric formed by wet oxidation techniques, even at a reduced thickness. In certain embodiments, the radical oxidation process is carried out in a batch-processing chamber or furnace capable of processing multiple substrates to provide a high quality tunnel dielectric 228 without impacting the throughput (wafers/hr.) requirements that a fabrication facility may require.

In another embodiment, tunnel dielectric layer 228 is deposited by chemical vapor deposition (CVD) or atomic layer deposition and is composed of a dielectric layer which may include, but is not limited to silicon dioxide, silicon oxy-nitride, silicon nitride, aluminum oxide, hafnium oxide, zirconium oxide, hafnium silicate, zirconium silicate, hafnium oxy-nitride, hafnium zirconium oxide and lanthanum oxide. In another embodiment, tunnel dielectric 228 is a bi-layer dielectric region including a bottom layer of a material such as, but not limited to, silicon dioxide or silicon oxy-nitride and a top layer of a material which may include, but is not limited to silicon nitride, aluminum oxide, hafnium oxide, zirconium oxide, hafnium silicate, zirconium silicate, hafnium oxy-nitride, hafnium zirconium oxide and lanthanum oxide.

Referring again to FIG. 2D, a charge-trapping layer is formed on or overlying the tunnel dielectric 228. Generally, as in the embodiment shown, the charge-trapping layer is a multi-layer charge-trapping layer comprising multiple layers including at least a lower or first charge-trapping layer 230 a closer to the tunnel dielectric 228, and an upper or second charge-trapping layer 230 b that is oxygen-lean relative to the first charge-trapping layer and comprises a majority of a charge traps distributed in multi-layer charge-trapping layer.

The first charge-trapping layer 230 a of a multi-layer charge-trapping layer 230 can include a silicon nitride (Si₃N₄), silicon-rich silicon nitride or a silicon oxy-nitride (SiO_(x)N_(y) (H_(z))). For example, the first charge-trapping layer 230 a can include a silicon oxynitride layer having a thickness of between about 2.0 nm and about 4.0 nm formed by a CVD process using dichlorosilane (DCS)/ammonia (NH₃) and nitrous oxide (N₂O)/NH₃ gas mixtures in ratios and at flow rates tailored to provide a silicon-rich and oxygen-rich oxynitride layer.

The second charge-trapping layer 230 b of the multi-layer charge-trapping layer is then formed over the first charge-trapping layer 230 a. The second charge-trapping layer 230 b can include a silicon nitride and silicon oxy-nitride layer having a stoichiometric composition of oxygen, nitrogen and/or silicon different from that of the first charge-trapping layer 230 a. The second charge-trapping layer 230 b can include a silicon oxynitride layer having a thickness of between about 2.0 nm and about 5.0 nm, and may be formed or deposited by a CVD process using a process gas including DCS/NH₃ and N₂O/NH₃ gas mixtures in ratios and at flow rates tailored to provide a silicon-rich, oxygen-lean top nitride layer.

As used herein, the terms “oxygen-rich” and “silicon-rich” are relative to a stoichiometric silicon nitride, or “nitride,” commonly employed in the art having a composition of (Si₃N₄) and with a refractive index (RI) of approximately 2.0. Thus, “oxygen-rich” silicon oxynitride entails a shift from stoichiometric silicon nitride toward a higher wt. % of silicon and oxygen (i.e. reduction of nitrogen). An oxygen rich silicon oxynitride film is therefore more like silicon dioxide and the RI is reduced toward the 1.45 RI of pure silicon dioxide. Similarly, films described herein as “silicon-rich” entail a shift from stoichiometric silicon nitride toward a higher wt. % of silicon with less oxygen than an “oxygen-rich” film. A silicon-rich silicon oxynitride film is therefore more like silicon and the RI is increased toward the 3.5 RI of pure silicon.

Referring again to FIG. 2D, the number of dielectric layers further includes a cap layer 232 that is formed on or overlying the charge-trapping layer 230. In one embodiment, the cap layer 232 includes a silicon nitride all or part of which is subsequently oxidized to form a blocking oxide overlying the charge-trapping layer 230. The cap layer 232 can be a single layer of nitride (not shown) having a homogeneous composition, a single layer of nitride having a gradient in stoichiometric composition, or, as in the embodiment shown, can be a multi-layer cap layer including at least a lower or first cap layer 232 a overlying the second charge-trapping layer 230 b, and a second cap layer 232 b overlying the first cap layer 232 a.

In one embodiment, the first cap layer 232 a can include a silicon nitride, a silicon-rich silicon nitride or a silicon-rich silicon oxynitride layer having a thickness of between 2.0 nm and 4.0 nm formed by a CVD process using N₂O/NH₃ and DCS/NH₃ gas mixtures. Similarly, the second cap layer 232 b can also include a silicon nitride, a silicon-rich silicon nitride or a silicon-rich silicon oxynitride layer having a thickness of between 2.0 nm and 4.0 nm formed by a CVD process using N₂O/NH₃ and DCS/NH₃ gas mixtures. Optionally, the first cap layer 232 a and second cap layer 232 b can comprise different stoichiometries. For example, the second cap layer 232 b can comprise a silicon or oxygen rich composition relative to the first cap layer 232 a to facilitate removal of the second cap layer in a dry or wet clean process prior to oxidizing the first cap layer. Alternatively, the first cap layer 232 a can comprise a silicon or oxygen rich composition relative to the second cap layer 232 b to facilitate oxidation of the first cap layer.

Referring to FIG. 2E, a sacrificial oxide layer 234 is formed on or overlying the second cap layer 232 b. In one embodiment, the sacrificial oxide layer 234 can include a silicon dioxide layer grown by a thermal oxidation process, in-situ steam generation (ISSG), or radical oxidation, and having a thickness of between 2.0 nm and 4.0 nm. In another embodiment, the sacrificial oxide layer 234 can be formed or deposited by a chemical vapor deposition process in a low pressure chemical vapor deposition (LPCVD) chamber. For example, the sacrificial oxide layer 234 can be deposited by a CVD process using a process gas including gas mixtures of silane or DCS and an oxygen containing gas, such as O₂ or N₂O, in ratios and at flow rates tailored to provide a silicon dioxide (SiO₂) sacrificial oxide layer.

Next, referring to FIG. 2F, a patterned mask layer (not shown) is formed on or overlying the sacrificial oxide layer 234, and the sacrificial oxide, cap layer 232, and the charge-trapping layer 230 etched or patterned to form a gate stack 236 overlying the channel 224 of the NVM transistor and to remove the sacrificial oxide, cap layer, and the charge trapping layers 230 from the second region 208 of the substrate 204. The patterned mask layer can include a photoresist layer patterned using standard lithographic techniques, and the sacrificial oxide layer 234, cap layer 232, and the charge trapping layers 230 from can be etched or removed using a dry etch process including one or more separate steps to stop on the surface 216 of the substrate 204.

Referring to FIG. 1, a gate oxide or GOX preclean is performed, gate oxides for both MOS transistors 214, 212 formed, and a gate layer is deposited and patterned to form gates for the NVM transistor 226, and both MOS transistors (step 110). Referring to FIG. 2G, the GOX preclean removes the sacrificial oxide layer 234 and a portion of the cap layer 232 or substantially of all of a top most layer in a multi-layer cap layer are removed from the gate stack 236 in a highly selective cleaning process. This cleaning process simultaneously or concurrently further removes any oxide, such as an oxide tunnel dielectric 228 and pad oxide 209, remaining in the first region 206 outside the gate stack 236 and in the second region 208 to prepare the substrate 204 in that region for gate oxide growth. The thickness of the cap layer 232 is adjusted to allow a portion or substantially all of the second cap layer 232 b to be consumed by the GOX preclean. In one exemplary implementation the sacrificial oxide layer 234 and the second cap layer 232 b are removed in a wet clean process using a 10:1 buffered oxide etch (BOE) containing a surfactant. Alternatively, the wet clean process can be performed using a 20:1 BOE wet etch, a 50:1 hydrofluoric (HF) wet etch, a pad etch, or any other similar hydrofluoric-based wet etching chemistry.

This embodiment of the GOX preclean is advantageous in that it substantially does not affect the baseline CMOS process—either in the preclean step (step 110) or a subsequent oxidation step (step 112), but rather uses it for the integration of the NVM transistor fabrication.

Next, referring to FIG. 2H, an oxidation process is performed to oxidize the remaining portion of the cap layer 232 or the first cap layer 232 a of a multi-layer cap layer, and a portion of the second charge-trapping layer 230 b to form a blocking oxide layer 238 overlying the second charge-trapping layer. In one embodiment, the oxidation process is adapted to oxidize the first cap layer 232 a to form the blocking oxide layer 238 while simultaneously or concurrently oxidizing at least a portion of the surface 216 of the substrate 204 in the second region 208 to form a first gate oxide 240 overlying at least the channel 218 of at least one MOS transistor. The oxidation process can include in-situ-steam-generation (ISSG), CVD, or radical oxidation performed in a batch or single substrate processing chamber with or without an ignition event such as plasma. For example, in one embodiment the blocking oxide layer 238 and the gate oxide 240 may be grown in a radical oxidation process involving flowing hydrogen (H₂) and oxygen (O₂) gas into a processing chamber at a ratio to one another of approximately 1:1 without an ignition event, such as forming of a plasma, which would otherwise typically be used to pyrolyze the H₂ and O₂ to form steam. Instead, the H₂ and O₂ are permitted to react at a temperature approximately in the range of 700-800° C. at a pressure approximately in the range of 0.5-5 Torr to form radicals, such as, an OH radical, an HO₂ radical or an O diradical radicals at a surface of the cap layer 232 or the first cap layer 232 a. The oxidation process is carried out for a duration approximately in the range of 1-5 minutes for a single substrate using an ISSG process, or 10-15 minutes for a batch furnace process to effect growth of a blocking oxide layer 238 by oxidation and consumption of the first cap layer 232 a and a portion of the second charge-trapping layer 230 b having a thickness of from about 3 nm to about 4.5 nm, and gate oxide 240 having a thickness of from about 5 nm to about 7 nm.

In some embodiments, such as that shown in FIGS. 2I to 2L, the method further includes a dual gate oxide process flow to enable fabrication of both a LV MOS transistor 212 and a HV MOS transistor 214. Referring to FIG. 2I, a patterned mask layer 242 is formed over the first and second regions 206, 208 of the substrate 204. The patterned mask layer 242 can be a photoresist layer patterned using standard lithographic techniques, and includes at least one opening 244 over a channel 218 in the second region 208. The thick, first gate oxide 240 is etched in the exposed regions by using a BOE etch, under conditions similar to those described above with respect to removing the sacrificial oxide layer 234, and the patterned mask layer 242 is then removed.

Referring to FIG. 2J, the substrate 206 is cleaned using a wet etch that does not etch oxide in order to protect the first gate oxide 240 of the HV MOS transistor 212, and the blocking oxide layer 238 of the gate stack 236. The substrate 206 is then subjected to a thermal oxidation process to grow a thin, second gate oxide 246 having a thickness from about 1 nm to about 3 nm. In some embodiments, the second gate oxide 246 can be overlaid with a deposited layer (not shown) such as silicon oxy-nitride, silicon nitride, aluminum oxide, hafnium oxide, zirconium oxide, hafnium silicate, zirconium silicate, hafnium oxy-nitride, hafnium zirconium oxide and lanthanum oxide.

Referring to FIG. 2K, a gate layer 248 of any conducting or semiconducting material suitable for accommodating a biasing of the NVM transistor 226 and operation of the MOS transistors 214, 212, is formed over the gate stack 236, the first gate oxide 240 of the HV MOS transistor 214, and the second gate oxide 246 of the MOS transistor 212. In one embodiment, the gate layer is formed by physical vapor deposition and is composed of a metal-containing material which may include, but is not limited to, metal nitrides, metal carbides, metal silicides, hafnium, zirconium, titanium, tantalum, aluminum, ruthenium, palladium, platinum, cobalt and nickel. In another embodiment, the gate layer is formed by a CVD process and is composed of a single doped polysilicon layer, which may then be patterned to form control gates of the NVM transistor 226 and MOS transistors 214, 212.

Referring to FIG. 2L, the gate layer 248 is patterned using a mask layer (not shown) and standard lithographic techniques to stop on surfaces of the blocking oxide layer 238, the first gate oxide 240 and the second gate oxide 246, thereby forming a gate 250 for the gate stack 236 of a NVM transistor 226, a gate 252 for the HV MOS transistor 214, and a gate 254 for the MOS transistor 212.

Referring to FIG. 1 and FIG. 2M, a first spacer layer is deposited and etched to form first sidewall spacers 256 adjacent to the gates 252, 254, of the MOS transistors 212, 214, and the NVM transistor 226, and one or more lightly-doped drain extensions (LDD 258) are implanted adjacent to and extend under sidewall spacers 256 of one or more of the MOS transistors 212, 214 (step 112).

Next, a SONOS LDD mask is formed over the substrate 204 and lightly-doped drain extensions (LDD 260) are implanted, adjacent to the NVM transistor 226. Finally, a second spacer layer is deposited and etched to form second sidewall spacers 262 adjacent to the gate stack 236, of the NVM transistor 226 (step 114).

Referring to FIGS. 1 and 2N, with the NVM transistor 226, HV MOS transistor 214 and MOS transistor 212 substantially complete, source and drain implants are performed to form source and drain regions 264 for all transistors and a silicide process performed (step 116). As depicted, silicide regions 266 may be formed on the exposed gates 250, 252 and 254 and exposed source and drain regions 264. The silicide process may be any commonly employed in the art, typically including a pre-clean etch, cobalt or nickel metal deposition, anneal and wet strip.

Referring FIG. 1 and FIG. 2N, optionally the method of fabricating memory cells including an embedded or integrally formed SONOS based NVM transistor and MOS transistors further includes the step of forming a stress inducing layer or structure 268, such as a stress inducing nitride layer, over the gate stack 236 of the NVM transistor 226 to increase data retention and/or to improve programming time and efficiency (step 118). In particular, inducing stress into the charge-trapping layer 230 of the NVM transistor 226 changes energy levels of charge traps formed therein, thereby increasing charge retention of the charge-trapping layer. In addition, forming a stress inducing structure 268, in or on the surface 216 of the substrate 204 proximal to, and preferably surrounding, a region of the substrate in which the channel 224 of NVM transistor 226 is formed will reduce the band gap, and, depending on the type of strain, increases carrier mobility. For example, tensile strain, in which inter-atomic distances in the crystal lattice of the substrate 204 are stretched, increases the mobility of electrons, making N-type transistors faster. Compressive strain, in which those distances are shortened, produces a similar effect in P-type transistors by increasing the mobility of holes. Both of these strain induced factors, i.e., reduced band gap and increased carrier mobility, will result in faster and more efficient programming of NVM transistor 226.

The strain inducing structure 268 can include a pre-metal dielectric (PMD) layer formed using a High Aspect Ratio Process (HARP™) oxidation process, a compressive or tensile nitride layer formed using a plasma enhanced chemical vapor deposition (PECVD) or a Bis-TertiaryButylAmino Silane (BTBAS) nitride layer.

In certain embodiments, such as that shown in FIG. 2N, the stress inducing structure 268 may also be formed over one or more of the MOS transistors to induce strain in the channel of the MOS transistor.

Finally, the standard or baseline CMOS process flow is continued to substantially complete the front end device fabrication (step 120), yielding the structure shown in FIG. 2N. FIG. 2N is a block diagram illustrating a cross-sectional view of a portion of a finished memory cell including an embedded SONOS based NVM transistor and MOS transistors fabricated according to the method of FIGS. 1 and 2A-2M.

FIGS. 3A and 3B are graphs illustrating improvements in threshold voltage (V_(T)) uniformity of an NVM transistor including an indium channel according to an embodiment of the present disclosure. Referring FIGS. 3A and 3B it is noted that the heavier Indium atom does not move or diffuse as much as a light Boron atoms used in prior n-channel SONOS based NVM transistors, in the subsequent high temperature steps and hence the random dopant effects are reduced, significantly improving the V_(T) uniformity from a sigma of V_(T) from ˜150 mV to ˜70 to 80 mV.

FIGS. 4A-4C are graphs illustrating basic program erase characteristics and showing improvements in endurance and data retention for a memory device including an embedded SONOS based NVM transistor fabricated according to an embodiment of the present disclosure. In particular, FIG. 4A shows subthreshold characteristics of the SONOS based NVM transistor in both the programmed and erased states. This figure shows a good subthreshold slope of about 135 mV is achieved using Indium implant which is one of the embodiments of the present disclosure.

FIG. 4B shows the cycling endurance of the SONOS NVM transistor fabricated according to an embodiment of the process described previously. It can be seen from FIG. 4B that there is no significant change in threshold voltage (V_(T)) on either program or erase after 100 thousand program and erase (P/E) cycles.

FIG. 4C shows the data retention charge loss for SONOS based NVM transistor fabricated according to an embodiment of the present disclosure. Referring to FIG. 4C, the V_(T) window, i.e., a difference between the threshold voltage in programmed and erased states, is seen to be greater than 1V, which gives sufficient margin for error-free read even after 10 years or 3E8 seconds.

Thus, embodiments of memory cells including embedded or integrally formed SONOS based NVM transistor and MOS transistors and methods of fabricating the same have been described. Although the present disclosure has been described with reference to specific exemplary embodiments, it will be evident that various modifications and changes may be made to these embodiments without departing from the broader spirit and scope of the disclosure. Accordingly, the specification and drawings are to be regarded in an illustrative rather than a restrictive sense.

The Abstract of the Disclosure is provided to comply with 37 C.F.R. §1.72(b), requiring an abstract that will allow the reader to quickly ascertain the nature of one or more embodiments of the technical disclosure. It is submitted with the understanding that it will not be used to interpret or limit the scope or meaning of the claims. In addition, in the foregoing Detailed Description, it can be seen that various features are grouped together in a single embodiment for the purpose of streamlining the disclosure. This method of disclosure is not to be interpreted as reflecting an intention that the claimed embodiments require more features than are expressly recited in each claim. Rather, as the following claims reflect, inventive subject matter lies in less than all features of a single disclosed embodiment. Thus, the following claims are hereby incorporated into the Detailed Description, with each claim standing on its own as a separate embodiment.

Reference in the description to one embodiment or an embodiment means that a particular feature, structure, or characteristic described in connection with the embodiment is included in at least one embodiment of the circuit or method. The appearances of the phrase one embodiment in various places in the specification do not necessarily all refer to the same embodiment. 

What is claimed is:
 1. A device, comprising: a non-volatile memory (NVM) transistor formed in a first region of a substrate, the NVM transistor comprising an indium doped channel and a gate stack on the substrate overlying the channel, the gate stack including a dielectric layer on the substrate and a charge-trapping layer on the dielectric layer and an oxide layer overlying the charge-trapping layer, a first gate overlying the oxide layer, and a first silicide region overlying the first gate; a metal-oxide-semiconductor (MOS) transistor formed in a second region of the substrate, the MOS transistor comprising a gate oxide overlying the substrate in the second region, a second gate overlying the gate oxide, and a second silicide region overlying the second gate; and a nitride layer overlying at least directly over and in direct contact with the first silicide region of the NVM transistor.
 2. The device of claim 1, wherein the nitride layer is further disposed directly over and in direct contact with the second silicide region of the MOS transistor.
 3. The device of claim 1, wherein the MOS transistor is a low voltage transistor.
 4. The device of claim 1, wherein the MOS transistor is a high voltage transistor.
 5. The device of claim 1, wherein the MOS transistor is a p-channel transistor or a n-channel transistor.
 6. The device of claim 1, wherein the charge-trapping layer is a multi-layer structure, the charge-trapping layer includes at least: a lower charge-trapping layer overlying the dielectric layer, the lower charge-trapping layer comprising silicon nitride, silicon-rich nitride, silicon oxy-nitride or a combination thereof; and an upper charge-trapping layer formed on the lower charge-trapping layer comprising silicon nitride, silicon oxy-nitride layer or a combination thereof, wherein the upper charge-trapping layer further includes a stoichiometric composition of oxygen, nitrogen or silicon content which is different from that of the lower charge-trapping layer, and wherein the upper charge-trapping layer is oxygen-lean compared to the lower charge-trapping layer.
 7. The device of claim 1, wherein the first gate and the second gate are formed concurrently.
 8. The device of claim 7, wherein the first gate and the second gate are formed by physical vapor deposition, the first gate and the second gate comprise a group of construction materials including: metal nitrides, metal carbides, metal silicides, hafnium, zirconium, titanium, tantalum, aluminum, ruthenium, palladium, platinum, cobalt, nickel and a combination thereof.
 9. The device of claim 7, wherein the first gate and the second gate are formed by a chemical vapor deposition (CVD) process including a single doped polysilicon layer.
 10. The device of claim 3, wherein the gate oxide of the low voltage MOS transistor includes high K dielectric selected from a group of: silicon oxy-nitride, silicon nitride, aluminum oxide, hafnium oxide, zirconium oxide, hafnium silicate, zirconium silicate, hafnium oxy-nitride, hafnium zirconium oxide and lanthanum oxide.
 11. A device, comprising: a NVM transistor formed in a first region of a substrate including a gate stack overlying an indium doped channel, a first gate overlying the gate stack, and a first silicide region overlying the first gate, wherein the gate stack includes a charge-trapping layer sandwiched between a top and a bottom dielectric layers; a MOS transistor pair formed in a second region of the substrate, wherein each of the MOS transistors includes a gate oxide overlying the substrate, a second gate overlying the gate oxide, and a second silicide region overlying the second gate of each of the MOS transistors; and a nitride layer overlying directly over and in direct contact with the first silicide region of the NVM transistor and each of the second silicide regions of the MOS transistors.
 12. The device of claim 11, wherein the top dielectric layer of the gate stack of the NVM transistor is formed concurrently with at least one of the gate oxides of the MOS transistor pair through an oxidation process.
 13. The device of claim 11, wherein the first gate and at least one of the second gates are formed concurrently.
 14. The device of claim 13, wherein the first gate and the second gates are formed by physical vapor deposition, the first gate and the second gates comprise a group of construction materials including: metal nitrides, metal carbides, metal silicides, hafnium, zirconium, titanium, tantalum, aluminum, ruthenium, palladium, platinum, cobalt, nickel and a combination thereof.
 15. The device of claim 13, wherein the first gate and the second gates are formed by a chemical vapor deposition (CVD) process including a single doped polysilicon layer.
 16. The device of claim 11, wherein the charge-trapping layer includes at least: a lower charge-trapping layer overlying the lower dielectric layer, the lower charge-trapping layer comprising silicon nitride, silicon-rich nitride, silicon oxy-nitride or a combination thereof; and an upper charge-trapping layer formed on the lower charge-trapping layer comprising silicon nitride, silicon oxy-nitride layer or a combination thereof, wherein the upper charge-trapping layer further includes a stoichiometric composition of oxygen, nitrogen or silicon content which is different from that of the lower charge-trapping layer, and wherein the upper charge-trapping layer is oxygen-lean compared to the lower charge-trapping layer.
 17. The device of claim 11, wherein at least one of the MOS transistors is a low voltage MOS transistor.
 18. The device of claim 11, wherein at least one of the MOS transistors is a high voltage MOS transistor.
 19. The device of claim 17, wherein the gate oxide of the low voltage MOS transistor includes high K dielectric selected from a group of: silicon oxy-nitride, silicon nitride, aluminum oxide, hafnium oxide, zirconium oxide, hafnium silicate, zirconium silicate, hafnium oxy-nitride, hafnium zirconium oxide and lanthanum oxide.
 20. A memory cell, comprising: a Silicon-Oxide-Nitride-Oxide-Silicon (SONOS) transistor formed in a first region of a substrate, the SONOS transistor comprising an indium doped channel and a gate stack on the substrate overlying the indium doped channel, a first gate and a first silicide region overlying the gate stack, the gate stack including a dielectric layer on the substrate, a lower and an upper charge-trapping layers on the dielectric layer, and an oxide layer overlying the upper charge-trapping layer; at least one metal-oxide-semiconductor (MOS) transistor formed in a second region of the substrate, each of the at least one MOS transistor comprising a gate oxide overlying the substrate, a second gate and a second silicide region overlying the gate oxide in the second region, wherein the gate oxide of the at least one MOS transistor and the oxide layer of the SONOS transistor are formed concurrently; and a nitride layer formed at least directly over and in direct contact with the first silicide region of the SONOS transistor and the second silicide region of each of the at least one MOS transistor. 